BASF Ultramid® S3WG6 Balance 30% Glass Filled PA 610 (Dry)
Nylon 610, Glass Reinforced
BASF
产品说明：
Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. This means that more than 60 % of the base polymer for the product family consists of sustainable raw materials. Ultramid® S Balance is highly resistant to fuels, oils and greases, to most solvents, aqueous solutions and alkalis. Its resistance to weakly acid media makes it superior to PA 6 and PA 66.
Applications:
物性信息：
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.31 g/cc
0.0473 lb/in3
ISO 1183
吸水率
2.0 - 2.6 %
2.0 - 2.6 %
ISO 62
平衡吸湿
0.80 - 1.2 %
0.80 - 1.2 %
ISO 62
粘度测量
150
150
[cm<sup>3</sup>/g]; ISO 307
线性成型收缩率
0.0040 cm/cm
0.0040 in/in
Test Box 1.5 mm
线性成型收缩率,Flow
0.0040 cm/cm
0.0040 in/in
ISO 2577
线性成型收缩率，横向
0.0090 cm/cm
0.0090 in/in
ISO 2577
熔体流动速率
39.3 g/10 min
@Load 5.00 kg, Temperature 275 °C
39.3 g/10 min
@Load 11.0 lb, Temperature 527 °F
ISO 1133
机械性能
额定值 (公制)
额定值 (英制)
测试方法
抗张强度(断裂)
150 MPa
21800 psi
ISO 527-1/-2
屈服伸长率
4.0 %
4.0 %
ISO 527-1/-2
弹性模量
8.40 GPa
1220 ksi
ISO 527-1/-2
弯曲强度
230 MPa
33400 psi
ISO 178
弯曲模量
7.90 GPa
1150 ksi
ISO 178
简支梁无缺口冲击强度
8.50 J/cm2
@Temperature -30.0 °C
40.4 ft-lb/in2
@Temperature -22.0 °F
ISO 179/1eU
9.00 J/cm2
@Temperature 23.0 °C
42.8 ft-lb/in2
@Temperature 73.4 °F
ISO 179/1eU
简支梁缺口冲击强度
0.800 J/cm2
@Temperature -30.0 °C
3.81 ft-lb/in2
@Temperature -22.0 °F
ISO 179/1eA
1.30 J/cm2
@Temperature 23.0 °C
6.19 ft-lb/in2
@Temperature 73.4 °F
ISO 179/1eA
热性能
额定值 (公制)
额定值 (英制)
测试方法
熔融温度
220 °C
428 °F
ISO 11357-1/-3
加工性能
额定值 (公制)
额定值 (英制)
测试方法
加工（熔体）温度
270 - 290 °C
518 - 554 °F
Injection molding
模具温度
80.0 - 90.0 °C
176 - 194 °F
Injection molding/Extrusio