型材挤出 UTEC 6540 UTEC 5542F
UTEC6540 is an Ultra High Molecular Weight Polyethylene with a molecular weight greater than 10 times higher than High Density Polyethylene (HDPE) resins. This extremely high molecular weight yields several unique properties to this polymer such as high abrasion resistance, impact strength, and because it is a self-lubricating material, a low coefficient of friction.
Applications:
Applications which require highest wear resistance - technical parts RAM extruded and compression molded sheets, rods and profiles.
| 特性 |
超高分子量
低摩擦系数
良好抗撞击性
耐磨损性，良好
自润滑
|
| 用途 |
棒材
片材
型材
|
| 加工方法 |
挤出
片材挤出成型
型材挤出成型
压缩模塑
柱塞压出
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
| 密度 / 比重 |
0.925
|
g/cm3
|
ASTM D792 |
| 表观密度 |
0.45
|
g/cm3
|
ASTM D1895 |
| 固有粘度 |
28
|
dl/g
|
ASTM D4020 |
| 平均分子量 |
8000000
|
g/mol
|
内部方法 |
| 平均颗粒尺寸 - Dp50 4 |
230
|
μm
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
| 抗张强度 | ASTM D638, ISO 527-2 | ||
| 屈服 |
> 17.0
|
MPa
|
|
| 断裂 |
> 30.0
|
MPa
|
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
| 简支梁缺口冲击强度 5 |
> 100
|
J/m
|
ISO 11542-2 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
| 肖氏硬度 (邵氏 D, 15 秒) |
> 58
|
|
ASTM D2240, ISO 868 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
| 熔融峰值温度 |
133
|
°C
|
ASTM D3418 |