2363-55D 2363-90AE Pellethane
Available in Americas, Europe, Middle East, Africa, India and Asia
Data provided by Lubrizol
Lubrizol acquired the Pellethane product line from Dow in 2009.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.15 g/cc | 0.0415 lb/in3 | ASTM D792 |
| 线性成型收缩率,Flow |
0.0040 - 0.0080 cm/cm
@Thickness 1.60 mm
|
0.0040 - 0.0080 in/in
@Thickness 0.0630 in
|
|
| 线性成型收缩率，横向 |
0.0050 - 0.0060 cm/cm
@Thickness 1.60 mm
|
0.0050 - 0.0060 in/in
@Thickness 0.0630 in
|
|
| 熔体流动速率 |
8.0 - 18 g/10 min
@Load 2.16 kg, Temperature 224 °C
|
8.0 - 18 g/10 min
@Load 4.76 lb, Temperature 435 °F
|
ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 51 - 59 | 51 - 59 | ASTM D2240 |
| 极限抗拉强度 | 47.5 MPa | 6890 psi | ASTM D412 |
| 伸长率 (断裂) | 30 % | 30 % | ASTM D412 |
| 390 % | 390 % | ASTM D412 | |
| 50% Modulus | 0.0131 GPa | 1.90 ksi | ASTM D412 |
| 模量 | 0.0172 GPa | 2.49 ksi | ASTM D412 |
| 300％模量 | 0.0295 GPa | 4.28 ksi | ASTM D412 |
| 弯曲模量 | 0.172 GPa | 24.9 ksi | ASTM D790 |
| 撕裂强度 | 114 kN/m | 650 pli | Die "C"; ASTM D624 |
| 泰伯磨损，毫克/1000次 | 80 | 80 | H22 Wheel, 1000g; ASTM D1044 |
| 压缩 变形 |
25 %
@Temperature 25.0 °C, Time 79200 sec
|
25 %
@Temperature 77.0 °F, Time 22.0 hour
|
ASTM D395 Method B |
|
30 %
@Temperature 70.0 °C, Time 79200 sec
|
30 %
@Temperature 158 °F, Time 22.0 hour
|
ASTM D395 Method B |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 |
143 μm/m-°C
@Temperature 20.0 °C
|
79.4 μin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| 维卡软化温度 | 109 °C | 228 °F | ASTM D1525 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 210 - 225 °C | 410 - 437 °F | Molding |
| 模具温度 | 15.0 - 60.0 °C | 59.0 - 140 °F | |
| 干燥温度 | 90.0 - 105 °C | 194 - 221 °F |