BT-1172D Keyflex BT 1172D
|
Availability
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.25
|
g/cm3
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (240°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow (3.20 mm)
|
1.5 to 1.9
|
%
|
ASTM D955 |
|
Water Absorption (24 hr, 23°C, 50% RH)
|
0.30
|
%
|
ASTM D570 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness
|
|||
|
Shore D
|
66
|
|
ASTM D2240 |
|
Shore D, 15 sec
|
67
|
|
ISO 868 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength
|
|||
|
Yield, 2.00 mm 2
|
24.5
|
MPa
|
ASTM D638 |
|
Break, 2.00 mm 2
|
49.0
|
MPa
|
ASTM D638 |
|
Break, 2.00 mm
|
42.0
|
MPa
|
ISO 527-2/250 |
|
Tensile Elongation
|
|||
|
Break, 2.00 mm 2
|
600
|
%
|
ASTM D638 |
|
Break, 2.00 mm
|
> 500
|
%
|
ISO 527-2/250 |
|
Flexural Modulus
|
|||
|
6.40 mm 3
|
441
|
MPa
|
ASTM D790 |
|
-- 4
|
450
|
MPa
|
ISO 178 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tear Strength 2, 5
|
162
|
kN/m
|
ASTM D624 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact
|
|||
|
-40°C, 6.40 mm
|
44
|
J/m
|
ASTM D256 |
|
23°C, 6.40 mm
|
150
|
J/m
|
ASTM D256 |
|
-40°C
|
4.0
|
kJ/m2
|
ISO 180 |
|
23°C
|
20
|
kJ/m2
|
ISO 180 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed, 6.40 mm
|
130
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed
|
106
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
55.0
|
°C
|
ISO 75-2/A |
|
Melting Temperature
|
|||
|
-- 6
|
213
|
°C
|
ISO 11357-3 |
|
--
|
217
|
°C
|
ASTM D3418 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Volume Resistivity (23°C)
|
> 1.0E+13
|
ohms·cm
|
ASTM D257 |
|
Dielectric Strength (23°C, 1.00 mm)
|
26
|
kV/mm
|
ASTM D149 |
|
Comparative Tracking Index (Solution A)
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.5 mm
|
HB
|
|
|
|
3.0 mm
|
HB
|
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80 to 90
|
°C
|
|
|
Drying Time
|
3.0 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.080
|
%
|
|
|
Rear Temperature
|
220 to 240
|
°C
|
|
|
Middle Temperature
|
230 to 250
|
°C
|
|
|
Front Temperature
|
235 to 255
|
°C
|
|
|
Nozzle Temperature
|
235 to 255
|
°C
|
|
|
Processing (Melt) Temp
|
220 to 240
|
°C
|
|
|
Mold Temperature
|
40 to 60
|
°C
|
|
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80 to 90
|
°C
|
|
|
Drying Time
|
3.0 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.060
|
%
|
|
|
Cylinder Zone 1 Temp.
|
220 to 240
|
°C
|
|
|
Cylinder Zone 2 Temp.
|
230 to 250
|
°C
|
|
|
Cylinder Zone 3 Temp.
|
230 to 250
|
°C
|
|
|
Cylinder Zone 4 Temp.
|
230 to 250
|
°C
|
|
|
Adapter Temperature
|
230 to 250
|
°C
|
|
|
Melt Temperature
|
220 to 240
|
°C
|
|
|
Die Temperature
|
220 to 240
|
°C
|