Optipro CP3510GM The Materials Group
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Appearance
|
|
|||
|
Forms
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.21
|
g/cm3
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
4.0
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow
|
0.35
|
%
|
ASTM D955 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Yield)
|
54.5
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break)
|
5.8
|
%
|
ASTM D638 |
|
Flexural Modulus
|
4590
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact
|
130
|
J/m
|
ASTM D256 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
71 to 82
|
°C
|
|
|
Drying Time
|
3.0 to 4.0
|
hr
|
|
|
Drying Time, Maximum
|
8.0
|
hr
|
|
|
Suggested Max Moisture
|
0.040
|
%
|
|
|
Suggested Shot Size
|
30 to 80
|
%
|
|
|
Rear Temperature
|
221 to 238
|
°C
|
|
|
Middle Temperature
|
227 to 243
|
°C
|
|
|
Front Temperature
|
232 to 260
|
°C
|
|
|
Nozzle Temperature
|
232 to 260
|
°C
|
|
|
Processing (Melt) Temp
|
221 to 238
|
°C
|
|
|
Mold Temperature
|
38 to 66
|
°C
|
|
|
Back Pressure
|
0.138 to 0.345
|
MPa
|
|
|
Cushion
|
5.08 to 12.7
|
mm
|
|
| Injection Notes | |||