抗紫外线Pibiflex 3567S2 Taro Plast
|
Availability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.12
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (220°C/2.16 kg)
|
25
|
cm3/10min
|
ISO 1133 |
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
0.90
|
%
|
ISO 62 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Shore Hardness (Shore D, 15 sec)
|
35
|
|
ISO 868 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress (Break)
|
18.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Break)
|
> 500
|
%
|
ISO 527-2/50 |
|
Flexural Modulus (23°C)
|
55.0
|
MPa
|
ISO 178 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress (Break)
|
18.0
|
MPa
|
ISO 37 |
|
Tensile Elongation (Break)
|
> 500
|
%
|
ISO 37 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Melting Temperature 1
|
195
|
°C
|
ISO 11357-3 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Oxygen Index
|
20
|
%
|
ISO 4589-2 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
100 to 110
|
°C
|
|
|
Drying Time
|
4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.050
|
%
|
|
|
Hopper Temperature
|
20 to 50
|
°C
|
|
|
Injection Feed Temperature
|
185 to 200
|
°C
|
|
|
Rear Temperature
|
185 to 200
|
°C
|
|
|
Middle Temperature
|
185 to 210
|
°C
|
|
|
Front Temperature
|
185 to 210
|
°C
|
|
|
Injection Zone 4 Temperature
|
185 to 215
|
°C
|
|
|
Nozzle Temperature
|
190 to 215
|
°C
|
|
|
Processing (Melt) Temp
|
200 to 220
|
°C
|
|
|
Mold Temperature
|
20 to 55
|
°C
|
|
|
Injection Rate
|
Moderate-Fast
|
|
|
|
Hot Runner
|
190 to 215
|
°C
|