DW-1032 NT000 食品级PARA
Filler / Reinforcement
|
|
|||
Features
|
|
|||
Uses
|
|
|||
Agency Ratings
|
|
|||
RoHS Compliance
|
|
|||
Appearance
|
|
|||
Forms
|
|
|||
Processing Method
|
|
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density
|
1.77
|
--
|
g/cm3
|
ISO 1183 |
Molding Shrinkage
|
0.10 to 0.30
|
--
|
%
|
ISO 294-4 |
Water Absorption (24 hr, 23°C)
|
0.13
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
24000
|
23000
|
MPa
|
ISO 527-1 |
Tensile Stress (Break)
|
280
|
250
|
MPa
|
ISO 527-2 |
Tensile Strain (Break)
|
1.8
|
2.0
|
%
|
ISO 527-2 |
Flexural Modulus
|
23500
|
--
|
MPa
|
ISO 178 |
Flexural Stress
|
400
|
--
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Notched Izod Impact
|
120
|
--
|
J/m
|
ASTM D256 |
Unnotched Izod Impact
|
900
|
--
|
J/m
|
ASTM D4812 |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
230
|
--
|
°C
|
ISO 75-2/A |
CLTE - Flow
|
1.4E-5
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Additional Information |
Dry
|
Conditioned
|
|
|
Moisture Absorption - Equil, 65% RH
|
--
|
|
|
Injection |
Dry
|
Unit
|
|
Drying Temperature
|
120
|
°C
|
|
Drying Time
|
0.50 to 1.5
|
hr
|
|
Rear Temperature
|
250 to 260
|
°C
|
|
Front Temperature
|
260 to 290
|
°C
|
|
Nozzle Temperature
|
260 to 290
|
°C
|
|
Processing (Melt) Temp
|
280
|
°C
|
|
Mold Temperature
|
120 to 140
|
°C
|
|
Injection Rate
|
Fast
|
|