Celanese MT1310 Vectra MT 1310

The Standard for the Industry. Excellent balance of properties, including easy flow, easy processing, thermal stability, chemical resistance, mechanical and electrical properties. Suitable for vapor phase surface mount electrical and electronic devices. 30% glass reinforced

Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
Celanese has established at the FDA a drug master file (DMF no.8468) and a Device Master File (MAF no.315) for Vectra MT1310. These are to assist our customers with their end use FDA petitions. Vectra MT1310 has been tested and complies with USP Class VI.

LCP外观为米黄色（也有呈白色的不透明的），密度为1.4~1.7g/cm3。聚合方法以熔融缩聚为主，全芳香族LCP多辅以固相缩聚以制得高分子量产品。非全芳香族LCP常采用一步或二步熔融聚合制取产品。近年连续熔融缩聚制取高分子量LCP的技术得到发展。  液晶芳香族聚酯在液晶态下由于其大分子链是取向的，它有异常规整的纤维状结构，性能特殊，制品强度很高，并不亚于金属和陶瓷。拉伸强度和弯曲模量可超过10年来发展起来的各种热塑性工程塑料。机械性能、尺寸稳定性、光学性能、电性能、耐化学药品性、阻燃性、加工性良好，耐热性好，热膨胀系数教低。采用的单体不同，制得的液晶聚酯的性能、加工性和价格也不同。选择的填料不同、填料添加量的不同也都影响它的性能。
  
LCP具有自增强性：具有异常规整的纤维状结构特点，因而不增强的液晶塑料即可达到甚至超过普通工程塑料用百分之几十玻璃纤维增强后的机械强度及其模量的水平。如果用玻璃纤维、碳纤维等增强，更远远超过其他工程塑料。
2）、液晶聚合物还具有优良的热稳定性、耐热性及耐化学药品性，对大多数塑料存在的蠕变特点，液晶材料可以忽略不计，而且耐磨、减磨性均优异。
3）、LCP的耐气候性、耐辐射性良好，具有优异的阻燃性，能熄灭火焰而不再继续进行燃烧。其燃烧等级达到UL94V-0级水平。
4）、LCP具有优良的电绝缘性能。其介电强度比一般工程塑料高，耐电弧性良好。在连续使用温度200-300℃，其电性能不受影响。间断使用温度可达316℃左右。
5)、LCP具有突出的耐腐蚀性能，LCP制品在浓度为90%酸及浓度为50%碱存在下不会受到侵蚀，对于工业溶剂、燃料油、洗涤剂及热水，接触后不会被溶解，也不会引起应力开裂。

成型加工1、干燥：140℃～140～150℃ /5-7Hr
2、注塑温度：260～300～410℃
3、模 温：100～100～240℃
LCP的成型温度高，因其品种不同，熔融温度在300~425℃范围内。LCP熔体粘度低，流动性好，与烯烃塑料近似。LCP具有极小的线膨胀系数，尺寸稳定性好。成型加工条件参考为：成型温度300~390℃；模具温度100~260℃；成型压力7~100MPa，压缩比2.5~4，成型收缩率0.1~0.6。

1、电子电气是LCP的主要市场：电子电气的表面装配焊接技术对材料的尺寸稳定性和耐热性有很高的要求（能经受表面装配技术中使用的气相焊接和红外焊接），用于微波炉容器；

4、LCP还可以与聚砜、PBT、聚酰胺等塑料共混制成合金，制件成型后其机械强度高，用以代替玻璃纤维增强的聚砜等塑料，既可提高机械强度性能，又可提高使用强度及化学稳定性等。目前正在研究将LCP用于宇航器外部的面板、汽车外装的制动系统等。