防火树脂 CYCOLAC ABS FR15U
| TYPICAL PROPERTIES (1) | |||
|
MECHANICAL机械性能
|
Value | Unit | Standard |
|
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
|
37
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
|
30
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
|
2.4
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
|
17
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
|
2060
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
|
67
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
|
2340
|
MPa
|
ASTM D 790
|
|
Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min
|
41
|
MPa
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
|
21.9
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
|
2210
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
|
63
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
|
2260
|
MPa
|
ISO 178
|
|
IMPACT
|
Value | Unit | Standard |
|
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
|
213
|
J/m
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C
|
28
|
J
|
ASTM D 3763
|
|
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度，80*10*4 +23°C
|
12
|
kJ/m2
|
ISO 180/1A
|
|
THERMAL
|
Value | Unit | Standard |
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
93
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
|
86
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
|
75
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
|
9.E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
|
9.18E-05
|
1/°C
|
ASTM E 831
|
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
92
|
°C
|
ISO 306
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
90
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
85
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
90
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value | Unit | Standard |
|
Specific Gravity/比重
|
1.19
|
–
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率, 230°C/3.8 kgf
|
3.3
|
g/10 min
|
ASTM D 1238
|
|
Melt Viscosity, 200°C, 1000 sec-1
|
3200
|
poise
|
ASTM D 3825
|
|
Density/密度
|
1.19
|
g/cm3
|
ISO 1183
|
|
Melt Flow Rate / 熔流率, 220°C/5.0 kg
|
7
|
g/10 min
|
ISO 1133
|
|
Melt Volume Rate, MVR at 220°C/10.0 kg / 溶化体积流率,MVR, 220°C/10.0 kg
|
40
|
cm3/10 min
|
ISO 1133
|
|
ELECTRICAL
|
Value | Unit | Standard |
|
Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition {PLC) / 热丝引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate {PLC} / 高电压电弧起痕速率
|
4
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}
|
4
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
Volume Resistivity/体积电阻率
|
>1.E+14
|
Ohm-cm
|
IEC 60093
|
|
Dielectric Strength, in oil, 3.2 mm / 耐电强度，在油中，3.2mm
|
20
|
kV/mm
|
IEC 60243-1
|
|
FLAME CHARACTERISTICS 火焰特性
|
Value | Unit | Standard |
|
UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
|
1.49
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3) / UL认可,94-5VA 阻燃等级(3)
|
2.79
|
mm
|
UL 94
|
|
Source GMD, last updated:12/08/2005
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature / 干燥温度
|
80 – 90
|
°C
|
|
Drying Time / 干燥时间
|
2 – 4
|
hrs
|
|
Drying Time (Cumulative) / 干燥时间（累积的）
|
8
|
hrs
|
|
Maximum Moisture Content / 含湿量
|
0.01
|
%
|
|
Melt Temperature / 熔体温度
|
205 – 230
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
205 – 230
|
°C
|
|
Front – Zone 3 Temperature / 前区3温度
|
205 – 220
|
°C
|
|
Middle – Zone 2 Temperature / 中区2温度
|
200 – 210
|
°C
|
|
Rear – Zone 1 Temperature / 后区1温度
|
170 – 180
|
°C
|
|
Mold Temperature / 模具温度
|
50 – 70
|
°C
|
|
Back Pressure / 背压
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺杆速度
|
30 – 60
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
|
50 – 70
|
%
|
|
Vent Depth / 排气孔深度
|
0.038 – 0.051
|
mm
|