Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min

44

MPa

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min

33

MPa

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min

2

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min

24

%

ASTM D 638

Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min

2270

MPa

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距

72

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距

2340

MPa

ASTM D 790

Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C

320

J/m

ASTM D 256

Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C

30

J

ASTM D 3763

Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50

98

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火

96

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火

82

°C

ASTM D 648

CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动

8.82E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向

8.82E-05

1/°C

ASTM E 831

Relative Temp Index, Elec / 相对热指数， 电性能

60

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

60

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

60

°C

UL 746B

Specific Gravity/比重

1.04

–

ASTM D 792

Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm

0.5 – 0.8

%

SABIC Method

Melt Flow Rate / 熔流率, 230°C/3.8 kgf

5.6

g/10 min

ASTM D 1238

Melt Viscosity, 240°C, 1000 sec-1

2250

poise

ASTM D 3825

Melt Flow Rate / 熔流率, 220°C/10.0 kg

18

g/10 min

ISO 1133

Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC}

6

PLC Code

ASTM D 495

Hot Wire Ignition {PLC) / 热丝引燃 {PLC)

3

PLC Code

UL 746A

High Voltage Arc Track Rate {PLC} / 高电压电弧起痕速率

3

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}

0

PLC Code

UL 746A

UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3)

1.52

mm

UL 94

Drying Temperature / 干燥温度

80 – 95

°C

Drying Time / 干燥时间

2 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / *含湿量

0.01

%

Melt Temperature / 熔体温度

220 – 260

°C

Nozzle Temperature / 注嘴温度

220 – 260

°C

Front – Zone 3 Temperature / 前区3温度

215 – 240

°C

Middle – Zone 2 Temperature / 中区2温度

205 – 225

°C

Rear – Zone 1 Temperature / 后区1温度

190 – 210

°C

Mold Temperature / 模具温度

50 – 70

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

30 – 60

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

50 – 70

%

Vent Depth / 排气孔深度

0.038 – 0.051

mm