沙比克耐刮擦 DMX9254 LEXAN DMX6014
东莞市苏广塑胶原料有限公司长期供应PC 聚碳酸酯 系列：
注塑级PC/挤出级PC/吹塑级PC/脱模级PC/透明PC/瓷白PC/黑色PC/防火阻燃PC
耐高温PC/耐低温PC/光扩散PC/医疗级PC/加纤PC/食品级PC/玻纤增强PC/耐寒PC
耐老化PC/耐磨PC/抗冲击PC/防紫外线PC/高流动PC/高粘度PC/低粘度PC/板材PC
光学级PC/耐水解PC
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| 密度 | 1.17 g/cc | 0.0423 lb/in3 | ASTM D 792 |
| 1.17 g/cc | 0.0423 lb/in3 | ISO 1183 | |
| 吸水率 | 0.080 % @Time 86400 sec | 0.080 % @Time 24.0 hour | ASTM D 570 |
| 平衡吸湿 | 0.13 % | 0.13 % | 23°C / 50% RH; ISO 62 |
| 0.13 % | 0.13 % | 50% RH; ASTM D 570 | |
| 0.28 % @Temperature 23.0 °C | 0.28 % @Temperature 73.4 °F | ASTM D 570 | |
| 0.040 % @Time 86400 sec | 0.040 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| 饱和吸水率 | 0.27 % @Temperature 23.0 °C | 0.27 % @Temperature 73.4 °F | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 13 g/10 min @Load 1.20 kg, Temperature 300 °C | 13 g/10 min @Load 2.65 lb, Temperature 572 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 14.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 14.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | ASTM D 785 |
| 洛氏硬度（M 级） | 93 | 93 | ASTM D 785 |
| 硬度，H358/30 | 128 MPa | 18600 psi | ISO 2039-1 |
| 抗张强度(断裂) | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| 抗张强度(屈服) | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D 638 |
| 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 40 % | 40 % | 50 mm/min; ISO 527 |
| 70 % | 70 % | Type I, 50 mm/min; ASTM D 638 | |
| 屈服伸长率 | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| 2.90 GPa | 421 ksi | 50 mm/min; ASTM D 638 | |
| 弯曲强度 | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
| 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 |
| 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 | 0.300 J/cm @Temperature 23.0 °C | 0.562 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 0.300 J/cm @Temperature -30.0 °C | 0.562 ft-lb/in @Temperature -22.0 °F | ASTM D 256 | |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D 4812 |
| 悬壁梁缺口冲击强度 | 4.00 kJ/m2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | 80*10*3; ISO 180/1A |
| 5.00 kJ/m2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | 80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | 45.0 kJ/m2 @Temperature -30.0 °C | 21.4 ft-lb/in2 @Temperature -22.0 °F | 80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 80*10*3; ISO 180/1U | |
| 简支梁无缺口冲击强度 | 4.70 J/cm2 @Temperature -30.0 °C | 22.4 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.300 J/cm2 @Temperature 23.0 °C | 1.43 ft-lb/in2 @Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | 30.0 J @Temperature 23.0 °C | 22.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 10 @Load 1.00 kg | 10 @Load 2.20 lb | CS-17; ASTM D 1044 |
| 10 @Load 1.00 kg | 10 @Load 2.20 lb | CS-17; SABIC Method |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 70.0 μm/m-°C @Temperature -40.0 - 95.0 °C | 38.9 μin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 70.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 70.0 μm/m-°C @Temperature -40.0 - 95.0 °C | 38.9 μin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 70.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 比热容 | 1.40 J/g-°C | 0.335 BTU/lb-°F | ASTM C 351 |
| 导热系数 | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | ASTM C 177 |
| 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | ISO 8302 | |
| Hot Ball Pressure Test | <= 140 °C | <= 284 °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 133 °C @Thickness 3.20 mm | 271 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 119 °C @Thickness 3.20 mm | 246 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 维卡软化温度 | 138 °C | 280 °F | Rate B/50; ISO 306 |
| 139 °C | 282 °F | Rate B/50; ASTM D 1525 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | UL 94 by SABIC-IP |
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL 94 by SABIC-IP |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.584 | 1.584 | ASTM D 542 |
| 1.584 | 1.584 | ISO 489 | |
| 雾度 | <= 0.80 % @Thickness 2.54 mm | <= 0.80 % @Thickness 0.100 in | ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm | 88 % @Thickness 0.100 in | ASTM D 1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | Passes | IEC 60695-10-2 |
| Erichson scratch depth, 6N, micrometer | 14 | SABIC Method |
| Pencil Hardness test, 1kgf | H | ASTM D 3363 |