Application: Automotive (Bumper Back Beam)
CAS No. 30965-26-5, 103598-77-2 and 65997-17-3
Information provided by LG Chemical
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| 处理 | 0.020 | 0.020 | Injection Molding |
| 线性成型收缩率,Flow | 0.0070 - 0.010 cm/cm @Thickness 3.20 mm | 0.0070 - 0.010 in/in @Thickness 0.126 in | ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 81.4 MPa @Thickness 3.20 mm | 11800 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| 伸长率 (断裂) | >= 6.0 % @Thickness 3.20 mm | >= 6.0 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
| 弯曲强度 | 127 MPa @Thickness 6.40 mm | 18500 psi @Thickness 0.252 in | 5mm/min; ASTM D790 |
| 弯曲模量 | 3.82 GPa @Thickness 6.40 mm | 555 ksi @Thickness 0.252 in | 5mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 10.8 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 20.2 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 225 °C | 437 °F | @ Break; ASTM D3418 |
| 载荷下热变形温度(1.8 MPa) | 110 °C @Thickness 6.40 mm | 230 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| 料筒中部温度 | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| 料筒前部温度 | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| 射嘴温度 | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| 加工（熔体）温度 | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| 模具温度 | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| 干燥温度 | 120 °C | 248 °F | Injection Molding |
| 干燥时间 | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |