Application: IT/OA (Housing)
CAS: 103598-77-2, 9003-56-9, 68928-70-1, 1309-64-4 and 65997-17-3
Information provided by LG Chemical
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| 处理 | 0.020 | 0.020 | Injection Molding |
| 线性成型收缩率,Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0040 in/in @Thickness 0.126 in | ASTM D955 |
| 熔体流动速率 | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 115 | 115 | ASTM D785 |
| 抗张强度(屈服) | 65.7 MPa @Thickness 3.20 mm | 9530 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| 伸长率 (断裂) | 7.0 % @Thickness 3.20 mm | 7.0 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
| 弯曲强度 | 108 MPa @Thickness 3.20 mm | 15600 psi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| 弯曲模量 | 3.92 GPa @Thickness 3.20 mm | 569 ksi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 0.686 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.29 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa) | 113 °C @Thickness 6.40 mm | 235 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| UL RTI | 60.0 °C @Thickness >=1.70 mm | 140 °F @Thickness >=0.0669 in | |
| UL RTI，机械冲击 | 60.0 °C @Thickness >=1.70 mm | 140 °F @Thickness >=0.0669 in | |
| UL RTI，机械无冲击 | 60.0 °C @Thickness >=1.70 mm | 140 °F @Thickness >=0.0669 in | |
| 可燃性(UL94) | V-0 @Thickness >=1.70 mm | V-0 @Thickness >=0.0669 in |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| 料筒中部温度 | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| 料筒前部温度 | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| 射嘴温度 | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| 加工（熔体）温度 | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| 模具温度 | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| 干燥温度 | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| 干燥时间 | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| 背压 | 0.00200 - 0.00600 MPa | 0.290 - 0.870 psi | Injection Molding |
| 螺杆转速 | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |