4069 TPEE Hytrel 40CB

2018-06-19

产品详情

产地美国
价格：30
产品名称4069 TPEE Hytrel 40CB 查看相似产品 >

简介

产品说明：

Hytrel® 4069 is a low modulus grade with nominal hardness of 40D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like injection molding and extrusion.

Information provided by DuPont Performance Polymers

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.11 g/cc	1.11 g/cc	ASTM D792
密度	1.11 g/cc	0.0401 lb/in3	ISO 1183
Water Absorption	0.20 % @Temperature 23.0 °C	0.20 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62
	0.70 % @Temperature 23.0 °C	0.70 % @Temperature 73.4 °F	Immersion 24h; ASTM D570
	0.70 % @Temperature 23.0 °C	0.70 % @Temperature 73.4 °F	Immersion 24h; ISO 62
	0.70 % @Temperature 23.0 °C	0.70 % @Temperature 73.4 °F	Saturation, immersed; ISO 62
线性成型收缩率	0.0080 cm/cm	0.0080 in/in	Flow; ASTM D955
线性成型收缩率,Flow	0.0080 cm/cm @Thickness 2.00 mm	0.0080 in/in @Thickness 0.0787 in	ISO 294-4
线性成型收缩率，横向	0.0080 cm/cm @Thickness 2.00 mm	0.0080 in/in @Thickness 0.0787 in	ISO 294-4
熔体流动速率	8.5 g/10 min @Load 2.16 kg, Temperature 220 °C	8.5 g/10 min @Load 4.76 lb, Temperature 428 °F	ASTM D1238
	8.5 g/10 min @Load 2.16 kg, Temperature 220 °C	8.5 g/10 min @Load 4.76 lb, Temperature 428 °F	ISO 1133
化合物熔体指数	7.7 g/10 min @Load 2.16 kg, Temperature 220 °C	7.7 g/10 min @Load 4.76 lb, Temperature 428 °F	cm3/10 min; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)	<= 37	<= 37	ISO 868
	<= 40	<= 40	ASTM D2240
	33 @Time 15.0 sec	33 @Time 0.00417 hour	ISO 868
抗张强度(断裂)	20.0 MPa @Temperature 23.0 °C	2900 psi @Temperature 73.4 °F	ASTM D638
	28.0 MPa @Temperature 23.0 °C	4060 psi @Temperature 73.4 °F	ISO 527 (1BA bar)
抗张强度	2.40 MPa @Strain 5.00 %, Temperature 23.0 °C	348 psi @Strain 5.00 %, Temperature 73.4 °F	ASTM D638
	3.20 MPa @Strain 10.0 %, Temperature 23.0 °C	464 psi @Strain 10.0 %, Temperature 73.4 °F	ISO 527 (1BA bar)
	3.50 MPa @Strain 10.0 %, Temperature 23.0 °C	508 psi @Strain 10.0 %, Temperature 73.4 °F	ASTM D638
	6.70 MPa @Strain 50.0 %, Temperature 23.0 °C	972 psi @Strain 50.0 %, Temperature 73.4 °F	ISO 527 (1BA bar)
伸长率 (断裂)	>= 50 % @Temperature 23.0 °C	>= 50 % @Temperature 73.4 °F	nominal; ISO 527 (1BA bar)
	>= 300 % @Temperature 23.0 °C	>= 300 % @Temperature 73.4 °F	ISO 527 (1BA bar)
	650 % @Temperature 23.0 °C	650 % @Temperature 73.4 °F	ISO 527 (1BA bar)
	700 % @Temperature 23.0 °C	700 % @Temperature 73.4 °F	ASTM D638
	800 % @Temperature 23.0 °C	800 % @Temperature 73.4 °F	nominal; ISO 527 (1BA bar)
拉伸模量	0.0450 GPa @Temperature 23.0 °C	6.53 ksi @Temperature 73.4 °F	ISO 527
弯曲模量	0.0280 GPa @Temperature 100 °C	4.06 ksi @Temperature 212 °F	ASTM D790
	0.0280 GPa @Temperature 100 °C	4.06 ksi @Temperature 212 °F	ISO 178
	0.0470 GPa @Temperature 23.0 °C	6.82 ksi @Temperature 73.4 °F	ISO 178
	0.0550 GPa @Temperature 23.0 °C	7.98 ksi @Temperature 73.4 °F	ASTM D790
	0.172 GPa @Temperature -40.0 °C	24.9 ksi @Temperature -40.0 °F	ASTM D790
	0.172 GPa @Temperature -40.0 °C	24.9 ksi @Temperature -40.0 °F	ISO 178
悬壁梁缺口冲击强度	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ASTM D256
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ASTM D256
	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ISO 180/1A
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 180/1A
简支梁无缺口冲击强度	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
简支梁缺口冲击强度	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ISO 179/1eA
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eA
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eA

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	4.00e+12 ohm-cm @Temperature 23.0 °C	4.00e+12 ohm-cm @Temperature 73.4 °F	IEC 60093
表面电阻	3.00e+14 ohm @Temperature 23.0 °C	3.00e+14 ohm @Temperature 73.4 °F	IEC 60093
介电常数	4.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	4.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	IEC 60250
	4.8 @Frequency 100 Hz, Temperature 23.0 °C	4.8 @Frequency 100 Hz, Temperature 73.4 °F	IEC 60250
介电强度	18.0 kV/mm @Temperature 23.0 °C	457 kV/in @Temperature 73.4 °F	IEC 60243-1
耗散因数	0.013 @Frequency 100 Hz, Temperature 23.0 °C	0.013 @Frequency 100 Hz, Temperature 73.4 °F	IEC 60250
	0.020 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	0.020 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	IEC 60250
相比耐漏电起痕指数(CTI)	>= 600 V @Temperature 23.0 °C	>= 600 V @Temperature 73.4 °F	IEC 60112
	>= 600 V @Thickness 3.00 mm, Temperature 23.0 °C	>= 600 V @Thickness 0.118 in, Temperature 73.4 °F	UL 746A

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	500 μm/m-°C @Temperature -40.0 - 23.0 °C	278 μin/in-°F @Temperature -40.0 - 73.4 °F	ASTM E 831
	500 μm/m-°C @Temperature 23.0 - 55.0 °C	278 μin/in-°F @Temperature 73.4 - 131 °F	ASTM E 831
	500 μm/m-°C @Temperature 55.0 - 120 °C	278 μin/in-°F @Temperature 131 - 248 °F	ASTM E 831
	500 μm/m-°C @Temperature -40.0 - 23.0 °C	278 μin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	500 μm/m-°C @Temperature 23.0 - 55.0 °C	278 μin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	500 μm/m-°C @Temperature 55.0 - 120 °C	278 μin/in-°F @Temperature 131 - 248 °F	ISO 11359-1/-2
线性热膨胀系数,横向流动	190 μm/m-°C @Temperature 23.0 - 55.0 °C	106 μin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	190 μm/m-°C @Temperature 55.0 - 120 °C	106 μin/in-°F @Temperature 131 - 248 °F	ISO 11359-1/-2
	192 μm/m-°C @Temperature 55.0 - 120 °C	107 μin/in-°F @Temperature 131 - 248 °F	ASTM E 831
	219 μm/m-°C @Temperature 23.0 - 55.0 °C	122 μin/in-°F @Temperature 73.4 - 131 °F	ASTM E 831
	270 μm/m-°C @Temperature -40.0 - 23.0 °C	150 μin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	277 μm/m-°C @Temperature -40.0 - 23.0 °C	154 μin/in-°F @Temperature -40.0 - 73.4 °F	ASTM E 831
熔融温度	193 °C	379 °F	10°C/min; ISO 11357-1/-3
	193 °C	379 °F	ASTM D3418
载荷下热变形温度(0.46 MPa)	50.0 °C	122 °F	ISO 75-1/-2
	55.0 °C	131 °F	ASTM D648
脆化温度	-95.0 °C	-139 °F	ISO 974
玻璃化转变温度，Tg	-50.0 °C	-58.0 °F	10°C/min; ISO 11357-1/-2
UL RTI	50.0 °C @Thickness 1.50 mm	122 °F @Thickness 0.0591 in	UL 746B
	50.0 °C @Thickness 3.00 mm	122 °F @Thickness 0.118 in	UL 746B

...