This data was supplied by SABIC-IP for the Americas region.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.27 g/cc | 0.0459 lb/in3 | ASTM D 792 |
| 1.27 g/cc | 0.0459 lb/in3 | ISO 1183 | |
| 平衡吸湿 | 0.50 % | 0.50 % | 23°C / 50% RH; ISO 62 |
| 0.37 % @Time 86400 sec | 0.37 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| 线性模具收缩，Flow | 0.021 cm/cm @Time 86400 sec | 0.021 in/in @Time 24.0 hour | ASTM D 955 |
| 0.0213 cm/cm @Time 86400 sec | 0.0213 in/in @Time 24.0 hour | ISO 294 | |
| 线性成型收缩率,横向 | 0.020 cm/cm @Time 86400 sec | 0.020 in/in @Time 24.0 hour | ASTM D 955 |
| 0.0205 cm/cm @Time 86400 sec | 0.0205 in/in @Time 24.0 hour | ISO 294 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 13.0 MPa | 1890 psi | ASTM D 638 |
| 14.0 MPa | 2030 psi | ISO 527 | |
| 屈服伸长率 | 39.9 % | 39.9 % | ISO 527 |
| 53.5 % | 53.5 % | ASTM D 638 | |
| 拉伸模量 | 0.200 GPa | 29.0 ksi | 50 mm/min; ASTM D 638 |
| 0.240 GPa | 34.8 ksi | 1 mm/min; ISO 527 | |
| 弯曲模量 | 0.260 GPa | 37.7 ksi | ASTM D 790 |
| 0.270 GPa | 39.2 ksi | ISO 178 | |
| 悬壁梁缺口冲击强度 | 2.40 J/cm @Temperature 23.0 °C | 4.50 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D 4812 |
| 悬壁梁缺口冲击强度 | 27.0 kJ/m2 @Temperature 23.0 °C | 12.8 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| 冲击试验 | 26.0 J | 19.2 ft-lb | Multiaxial Impact; ISO 6603 |
| 27.0 J @Temperature 23.0 °C | 19.9 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| 动态摩擦系数 | 0.47 | 0.47 | ASTM D 3702 Modified |
| 静态摩擦系数 | 0.45 | 0.45 | ASTM D 3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm3/N-M | 5.00 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 111 μm/m-°C @Temperature -40.0 - 40.0 °C | 61.7 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 111 μm/m-°C @Temperature -40.0 - 40.0 °C | 61.7 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 184 μm/m-°C @Temperature -40.0 - 40.0 °C | 102 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 184 μm/m-°C @Temperature -40.0 - 40.0 °C | 102 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 载荷下热变形温度(1.8 MPa) | 47.0 °C @Thickness 3.20 mm | 117 °F @Thickness 0.126 in | unannealed; ASTM D 648 |