2363-75D 聚醚基芳香族 热塑性聚氨酯
Available in Americas, Europe, Middle East, Africa, India and Asia
Data provided by Lubrizol
Lubrizol acquired the Pellethane product line from Dow in 2009.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| 线性成型收缩率,Flow | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| 线性成型收缩率，横向 | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| 熔体流动速率 | 28 g/10 min @Load 5.00 kg, Temperature 224 °C | 28 g/10 min @Load 11.0 lb, Temperature 435 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 76 | 76 | ASTM D2240 |
| 极限抗拉强度 | 40.0 MPa | 5800 psi | ASTM D412 |
| 伸长率 (断裂) | 380 % | 380 % | ASTM D412 |
| 弯曲模量 | 1.30 GPa | 189 ksi | ASTM D790 |
| 撕裂强度 | 257 kN/m | 1470 pli | Die C; ASTM D624 |
| 泰伯磨损，毫克/1000次 | 55 | 55 | H22 Wheel, 1000g; ASTM D1044 |
| Tensile Set | 50 % | 50 % | Elongation Set After Break; ASTM D412 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | 88.7 μm/m-°C @Temperature -80.0 - -30.0 °C | 49.3 μin/in-°F @Temperature -112 - -22.0 °F | ASTM D696 |
| 维卡软化温度 | 116 °C | 241 °F | 120°C/hr, 9.8N; ASTM D1525 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 204 - 221 °C | 399 - 430 °F | Extrusion |
| 210 - 227 °C | 410 - 441 °F | Molding | |
| 模具温度 | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| 干燥温度 | 99.0 - 110 °C | 210 - 230 °F | air dew point <-40°C |