产品展厅
产品展厅
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ISO1183 | 1.69 | g/cm3 | |
| 吸水率(平衡) | ISO62 | 0.28 | % | ||
| MoldShrinkage-Flow | InternalMethod | 0.10to0.30 | % | ||
| 机械性能 | 拉伸模量 | ISO527-2 | 20000 | MPa | |
| 抗张强度(屈服) | ASTMD638 | 248 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 2.3 | % | ||
| 弯曲模量 | ASTMD790 | 19300 | MPa | ||
| 弯曲强度(屈服) | ASTMD790 | 376 | MPa | ||
| 压缩模量 | ASTMD695 | 16500 | MPa | ||
| 压缩强度 | ASTMD695 | 328 | MPa | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | ASTMD256 | 120 | J/m | |
| 热性能 | 热变形温度(1.8MPa,未退火) | ISO75-2/A | 227 | °C | |
| 电气性能 | DielectricConstant2(2.40GHz) | ASTMD2520 | 4.44 | ||
| DissipationFactor2(2.40GHz) | ASTMD2520 | 0.012 | |||
| 相比耐漏电起痕指数(CTI)(3.00mm) | UL746 | >600 | V | ||
| 漏电起痕指数 | IEC60112 | >600 | V | ||
| UL746 | PLC0 | ||||
| 高电弧燃烧指数(HAI) | 0.400mm | UL746 | 37.6 | ||
| 0.750mm | UL746 | 53.6 | |||
| 1.50mm | UL746 | 70.2 | |||
| 3.00mm | UL746 | 95.4 | |||
| 0.40mm | UL746 | PLC2 | |||
| 0.75mm | UL746 | PLC2 | |||
| 1.5mm | UL746 | PLC1 | |||
| 3.0mm | UL746 | PLC1 | |||
| HighVoltageArcResistancetoIgnition(HVAR)(3.00mm) | UL746 | PLC0 | |||
| 高电压电弧起痕速率(HVTR)(3.00mm) | UL746 | PLC0 | |||
| 热丝引燃(HWI) | 0.400mm | UL746 | 95 | sec | |
| 0.750mm | UL746 | >120 | sec | ||
| 1.50mm | UL746 | >120 | sec | ||
| 3.00mm | UL746 | >120 | sec | ||
| 0.40mm | UL746 | PLC1 | |||
| 0.75mm | UL746 | PLC0 | |||
| 1.5mm | UL746 | PLC0 | |||
| 3.0mm | UL746 | PLC0 | |||
| 可燃性 | FlameRating3(0.40mm,ALL) | UL94 | V-0 | ||
| 热灯丝点火温度 | 0.40mm | IEC60695-2-13 | 775 | °C | |
| 0.75mm | IEC60695-2-13 | 800 | °C | ||
| 1.5mm | IEC60695-2-13 | 825 | °C | ||
| 3.0mm | IEC60695-2-13 | 850 | °C | ||
| 极限氧指数 | ISO4589-2 | 37 | % | ||
| ToxicGasEmissions | CO | BSS7239/ATS1000/ABD0031 | 100 | ppm | |
| HCL | BSS7239/ATS1000/ABD0031 | <1 | ppm | ||
| HCN | BSS7239/ATS1000/ABD0031 | 15 | ppm | ||
| HF | BSS7239/ATS1000/ABD0031 | <1 | ppm | ||
| NO+NO2 | BSS7239/ATS1000/ABD0031 | <1 | ppm | ||
| SO2 | BSS7239/ATS1000/ABD0031 | <1 | ppm | ||
| VerticalBurn-60second4(8.89cm) | DMS1510 | 5.0 | sec | ||