Tensile Stress, yield / 抗张程度,屈服, 5 mm/min

48

MPa

ISO 527

Tensile Stress, break / 抗张程度,断裂, 5 mm/min

39

MPa

ISO 527

Tensile Strain, yield / 拉伸伸长,屈服, 5 mm/min

2

%

ISO 527

Tensile Strain, break / 拉伸伸长,断裂, 5 mm/min

15.8

%

ISO 527

Tensile Modulus / 拉伸模量, 1 mm/min

2760

MPa

ISO 527

Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min

73

MPa

ISO 178

Flexural Modulus / 挠曲模量, 2 mm/min

2470

MPa

ISO 178

Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C

37

J

ASTM D 3763

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 +23°C

23

kJ/m2

ISO 180/1A

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 -30°C

8

kJ/m2

ISO 180/1A

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 -40°C

6

kJ/m2

ISO 180/1A

CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）

6.E-05

1/°C

ISO 11359-2

CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）

6.E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

98

°C

ISO 306

HDT（热变形温度）/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

81

°C

ISO 75/Af

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm (5)

0.4 – 0.6

%

SABIC Method

Density / 密度

1.05

g/cm3

ISO 1183

Drying Temperature / 干燥温度

80 – 95

°C

Drying Time / 干燥时间

2 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / *含湿量

0.02

%

Melt Temperature / 熔体温度

255 – 280

°C

Nozzle Temperature / 注嘴温度

255 – 280

°C

Front – Zone 3 Temperature / 前区3温度

250 – 270

°C

Middle – Zone 2 Temperature / 中区2温度

230 – 245

°C

Rear – Zone 1 Temperature / 后区1温度

215 – 230

°C

Mold Temperature / 模具温度

40 – 80

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

30 – 60

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

50 – 70

%

Vent Depth / 排气孔深度

0.038 – 0.051

mm