C2840 CYCOLOY C2801 PC/ABS挤出
CYCOLOY C2840 is a flame retardant PC+ABS grade without Chlorine or Bromine suitable for extrusion applications like sheet and profiles. It has an excellent processing window combined with a good property balance; high IMPACT, good heat resistance, UV and colour stability.
TYPICAL PROPERTIES (1) | |||
MECHANICAL机械性能 | Value | Unit | Standard |
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg | 60 | mg/1000cy | SABIC Method |
Tensile Stress, yield 5 mm/min / 抗张程度,屈服, 5 mm/min | 50 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min | 40 | MPa | ISO 527 |
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min | 57 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min | 40 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min | 3 | % | ISO 527 |
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min | 3 | % | ISO 527 |
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min | >20 | % | ISO 527 |
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min | 2750 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min | 82 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min | 2500 | MPa | ISO 178 |
Hardness, H358/30 / 球压硬度,H358/30 | 114 | MPa | ISO 2039-1 |
Hardness, Rockwell R / 硬度, 洛氏 R | 122 | – | ISO 2039-2 |
IMPACT | Value | Unit | Standard |
Izod IMPACT, notched 80*10*3 +23°C / 悬壁梁缺口冲击强度, 80*10*3 +23°C | 50 | kJ/m2 | ISO 180/1A |
Izod IMPACT, notched 80*10*3 -30°C / 悬壁梁缺口冲击强度, 80*10*3 -30°C | 12 | kJ/m2 | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*3 sp=62mm | 12 | kJ/m2 | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Thermal Conductivity / 导热系数 | 0.2 | W/m-°C | ISO 8302 |
CTE, 23°C to 60°C, flow / 线形膨胀系数,23°C 到60°C,流动 | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow / 线形膨胀系数,23°C 到60°C,横向 | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 75°C +/- 2°C | PASSES | – | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 | 93 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120 | 95 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 热变形温度,0.45 MPa, 未退火, 100 mm 跨距 | 92 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度,1.8 MPa, 未退火, 100 mm 跨距 | 75 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Mold Shrinkage on Tensile Bar, flow (2) / 收缩率,流动 | 0.5 – 0.7 | % | SABIC Method |
Density/密度 | 1.18 | g/cm3 | ISO 1183 |
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat) | 0.6 | % | ISO 62 |
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH) | 0.2 | % | ISO 62 |
Melt Volume Rate, MVR at 260°C/2.16 kg / 溶化体积流率,MVR, 260°C/2.16 kg | 15 | cm3/10 min | ISO 1133 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity/体积电阻率 | >1.E+15 | Ohm-cm | IEC 60093 |
Surface Resistivity, ROA / 表面电阻率 | >1.E+15 | Ohm | IEC 60093 |
Dielectric Strength, in oil, 0.8 mm / 耐电强度,在油中,0.8mm | 34 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 1.6 mm / 耐电强度,在油中,1.6mm | 26 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 3.2 mm / 耐电强度,在油中,3.2mm | 17 | kV/mm | IEC 60243-1 |
Relative Permittivity, 50/60 Hz / 相对介电常数,50/60 Hz | 2.8 | – | IEC 60250 |
Relative Permittivity, 1 MHz / 相对介电常数,1 MHz | 2.7 | – | IEC 60250 |
Dissipation Factor, 50/60 Hz / 耗散因素,50/60 Hz | 0.002 | – | IEC 60250 |
Dissipation Factor, 1 MHz / 耗散因素,1 MHz | 0.007 | – | IEC 60250 |
Comparative Tracking Index / 漏电起痕指数 | 600 | V | IEC 60112 |
FLAME CHARACTERISTICS 火焰特性 | Value | Unit | Standard |
UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3) | 1.5 | mm | UL 94 |
UL Recognized, 94-5VB Rating (3) / UL认可,94-5VB 阻燃等级(3) | 2.5 | mm | UL 94 |
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
Oxygen Index (LOI) / 极限氧指数 | 31 | % | ISO 4589 |
Source GMD, last updated:03/11/1999 |
Processing |
Parameter | ||
Profile Extrusion | Value | Unit |
Drying Temperature / 干燥温度 | 80 – 85 | °C |
Drying Time / 干燥时间 | 2 – 4 | hrs |
Melt Temperature / 熔体温度 | 230 – 260 | °C |
Barrel – Zone 1 Temperature / *气缸区温度 | 190 – 220 | °C |
Barrel – Zone 2 Temperature / 第2气缸区温度 | 210 – 240 | °C |
Barrel – Zone 3 Temperature / 第3气缸区温度 | 220 – 250 | °C |
Barrel – Zone 4 Temperature / 第4气缸区温度 | 230 – 260 | °C |
Hopper Temperature / 料筒温度 | 60 – 110 | °C |
Adapter Temperature / 连接器温度 | 230 – 260 | °C |
Die Temperature / 模具温度 | 220 – 250 | °C |
Calibrator Temperature | 50 – 70 | °C |