高流动PC/ABS C1000HF CYCOLOY C1000A
CYCOLOY C1000HF is a general purpose PC+ABS blend specially developed for thin wall applications requiring a high flow with a good balance of properties. It is suitable for applications in the automotive and appliance industry.
相关色号：C1000HF-701、C1000HF-100、C1000HF-WH7D163、C1000HF-86314、C1000HF-76701、C1000HF-7M1D155、C1000HF-YW8G002、C1000HF-96441、C1000HF-GY4G021
| TYPICAL PROPERTIES (1) | |||
MECHANICAL机械性能 | Value | Unit | Standard |
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg | 71 | mg/1000cy | SABIC Method |
Tensile Stress, yield 5 mm/min / 抗张程度，屈服, 5 mm/min | 50 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min | 40 | MPa | ISO 527 |
Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min | 45 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min | 4 | % | ISO 527 |
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min | 45 | % | ISO 527 |
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min | 4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min | 25 | % | ISO 527 |
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min | 86 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min | 2300 | MPa | ISO 178 |
Hardness, H358/30 / 球压硬度，H358/30 | 98 | MPa | ISO 2039-1 |
Hardness, Rockwell R / 硬度, 洛氏 R | 117 | – | ISO 2039-2 |
IMPACT | Value | Unit | Standard |
Izod IMPACT, notched 80*10*3 +23°C / 悬壁梁缺口冲击强度, 80*10*3 +23°C | 40 | kJ/m2 | ISO 180/1A |
Izod IMPACT, notched 80*10*3 -30°C / 悬壁梁缺口冲击强度, 80*10*3 -30°C | 15 | kJ/m2 | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度，23°C，C80*10*3 sp=62mm | 40 | kJ/m2 | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度，-30°C，C80*10*3 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Thermal Conductivity / 导热系数 | 0.2 | W/m-°C | ISO 8302 |
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动 | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向 | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 75°C +/- 2°C | PASSES | – | IEC 60695-10-2 |
Ball Pressure Test, approximate maximum | 100 | °C | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 | 114 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120 | 116 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 热变形温度，0.45 MPa, 未退火, 100 mm 跨距 | 117 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度，1.8 MPa, 未退火, 100 mm 跨距 | 95 | °C | ISO 75/Ae |
Relative Temp Index, Elec / 相对热指数， 电性能 | 60 | °C | UL 746B |
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能 | 60 | °C | UL 746B |
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能 | 60 | °C | UL 746B |
PHYSICAL | Value | Unit | Standard |
Mold Shrinkage on Tensile Bar, flow (2) / 收缩率，流动 | 0.5 – 0.7 | % | SABIC Method |
Density/密度 | 1.12 | g/cm3 | ISO 1183 |
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat) | 0.7 | % | ISO 62 |
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH) | 0.2 | % | ISO 62 |
Melt Volume Rate, MVR at 260°C/5.0 kg / 溶化体积流率,MVR, 260°C/5.0 kg | 24 | cm3/10 min | ISO 1133 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity/体积电阻率 | >1.E+15 | Ohm-cm | IEC 60093 |
Surface Resistivity, ROA / 表面电阻率 | >1.E+15 | Ohm | IEC 60093 |
Dielectric Strength, in oil, 0.8 mm / 耐电强度，在油中，0.8mm | 35 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 1.6 mm / 耐电强度，在油中，1.6mm | 25 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 3.2 mm / 耐电强度，在油中，3.2mm | 17 | kV/mm | IEC 60243-1 |
Relative Permittivity, 50/60 Hz / 相对介电常数，50/60 Hz | 2.8 | – | IEC 60250 |
Relative Permittivity, 1 MHz / 相对介电常数，1 MHz | 2.7 | – | IEC 60250 |
Dissipation Factor, 50/60 Hz / 耗散因素，50/60 Hz | 0.002 | – | IEC 60250 |
Dissipation Factor, 1 MHz / 耗散因素，1 MHz | 0.007 | – | IEC 60250 |
FLAME CHARACTERISTICS 火焰特性 | Value | Unit | Standard |
UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3) | 1.5 | mm | UL 94 |
UL Recognized, 94HB Flame Class Rating 2nd value (3) | 3 | mm | UL 94 |
Glow Wire Flammability Index / 灼热丝易燃指数 650°C, passes at | 3.2 | mm | IEC 60695-2-12 |
Source GMD, last updated:06/05/1998 |
Processing |
| Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature / 干燥温度 | 90 – 100 | °C |
Drying Time / 干燥时间 | 2 – 4 | hrs |
Maximum Moisture Content / *含湿量 | 0.02 | % |
Melt Temperature / 熔体温度 | 240 – 270 | °C |
Nozzle Temperature / 注嘴温度 | 220 – 260 | °C |
Front – Zone 3 Temperature / 前区3温度 | 230 – 270 | °C |
Middle – Zone 2 Temperature / 中区2温度 | 230 – 270 | °C |
Rear – Zone 1 Temperature / 后区1温度 | 210 – 240 | °C |
Hopper Temperature / 料筒温度 | 60 – 80 | °C |
Mold Temperature / 模具温度 | 60 – 90 | °C |